National Standard for Base Material (Embryo Material)|
Grade, Status
|
6063 T5 | ||||||||||||||||||||
|
Standard No.
|
GB5237.1-2008 | ||||||||||||||||||||
|
Appearance quality
|
The surface of the profile should be neat and tidy, and defects such as cracks, peeling, corrosion and air bubbles are not allowed. | ||||||||||||||||||||
| Slight crater, bump and scratch are allowed on the surface of the profile, which allows the depth decorative surface to be no more than 0.03mm, the non-decorative material surface to be no more than 0.07mm, and the mold extrusion mark depth to be no more than 0.03mm. | |||||||||||||||||||||
| The profile ends allow local deformation due to sawing and its longitudinal length should not exceed 20mm. | |||||||||||||||||||||
|
Dimensional tolerance deviation high precision
|
Plane clearance
|
Curvature
|
Twist
|
Angle
|
Length
|
||||||||||||||||
|
≤0.15mm at any width of 25mm
|
≤0.3mm at any length of 300mm
|
≤0.017mm at length of each meter
|
±1°
|
Nominal length ≤6m±15mm
|
|||||||||||||||||
|
Mechanical Properties
|
Webster hardness（HW）
|
Tensile Strength
|
Yield Strength
|
Elongation at Break
|
/
|
||||||||||||||||
|
≥8
|
≥160N/mm2
|
≥110N/mm2
|
8%
|
/
|
|||||||||||||||||
|
Chemical Composition
|
|
||||||||||||||||||||
National Standard for Anodic Oxidation and Coloring Profiles|
Grade, Status
|
6063 T5 | |||||||
|
Standard No.
|
GB5237.2-2008 | |||||||
|
Quality of substrate
|
Should comply with the GB5237.1-2008 | |||||||
|
Dimensional tolerance
|
Should comply with the GB5237.1-2008 | |||||||
|
Mechanical Properties
|
Should comply with the GB5237.1-2008 | |||||||
|
Chemical Composition
|
Should comply with the GB5237.1-2008 | |||||||
|
Chemical Composition
|
Average Film Thickness
|
Minimum Local Film Thickness
|
CASS Test
|
Drop Alkali Test
|
Falling Sand Experiment Wear Coefficient
|
Sealing
|
Appearance quality
|
|
|
Level AA10
|
≥10μm
|
≥8μm
|
≥Level 9
|
≥50S
|
≥300g/μm
|
≤30mg/dm2
|
The surface is not allowed to have burns, oxide film peeling and other defects affecting the use, and it is allowed to be partially free of film and electric burn within 80mm from the end of the profile. | |
|
Level AA15
|
≥15μm
|
≥12μm
|
≥Level 9
|
≥75S
|
≥300g/μm
|
/
|
||
National Standard for Powder Spraying Profiles|
Grade, Status
|
6063 T5 | |||||||||||
|
Standard No.
|
GB5237.2-2008 | |||||||||||
|
Quality of substrate
|
Should comply with the GB5237.1-2008 | |||||||||||
|
Dimensional tolerance
|
Should comply with the GB5237.1-2008 | |||||||||||
|
Mechanical Properties
|
After removing the coating, it should meet the GB5237.1-2008 | |||||||||||
|
Chemical Composition
|
After removing the coating, it should meet the GB5237.1-2008 | |||||||||||
|
Coating Performance
|
Coating Thickness(μm)
|
Color and Color Difference
|
Indentation Hardness (indentation resistance)
|
Adhesion
|
||||||||
|
Average Thickness
|
Maximum Local Thickness
|
Minimum Local Thickness
|
The coating color should be consistent with the standard color specified in the contract. |
≥80
|
Level 0
|
|||||||
|
≥60
|
≥120
|
≥40
|
/
|
/
|
||||||||
|
Chemical Composition
|
|
|||||||||||
Chemical Composition of Alloys|
Grade
|
Chemical Composition (mass fraction)(%) | ||||||||||
|
Si
|
Fe
|
Cu
|
Mn
|
Mg
|
Cr
|
Zn
|
Ti
|
Other
|
Al
|
||
|
/
|
/
|
/
|
/
|
/
|
/
|
/
|
/
|
Single
|
Total
|
Total
|
|
|
6063
|
0.20～0.6
|
0.35
|
0.1
|
0.1
|
0.45～0.9
|
0.1
|
0.1
|
0.1
|
0.05
|
0.15
|
Margin
|
|
6061
|
0.40～0.8
|
0.7
|
0.15～0.40
|
0.15
|
0.8～1.2
|
0.04～0.35
|
0.25
|
0.15
|
0.05
|
0.15
|
Margin
|
|
6005
|
0.6～0.9
|
0.35
|
0.1
|
0.1
|
0.40～0.6
|
0.1
|
0.1
|
0.1
|
0.05
|
0.15
|
Margin
|
|
6005A
|
0.50～0.9
|
0.35
|
0.5
|
0.5
|
0.40～0.7
|
0.3
|
0.2
|
0.1
|
0.05
|
0.15
|
Margin
|
|
6351
|
0.7～1.3
|
0.5
|
0.1
|
0.40～0.8
|
0.40～0.8
|
0.1
|
0.2
|
0.2
|
0.05
|
0.15
|
Margin
|